Research Article

Effect of Filler Content and Waiting time Before Light-Curing on Mechanical Properties of Dual-Cured Cement

Author(s): Ana C. de Assunção Oliveira, Sandro Griza, Rafael R. de Moraes and André L. Faria-e-Silva*

Volume 2, Issue 1, 2020

Page: [45 - 52] Pages: 8

DOI: 10.2174/2542579X01666190924180448

Price: $65

Abstract

Objective: To investigate the effect of filler content and the time spent before light-curing on mechanical properties of dual-cured cement.

Methods: Experimental dual-cured resin cements were formulated with 60, 65 or 68wt% of filler. The viscosity of experimental cement was measured using a digital viscometer. Bar-shaped specimens (25 x 2 x 2 mm) were fabricated, while the light-curing was started immediately or 5 minutes after the insertion of cement into the mold (n = 7). A three-point bending test was performed and the values of flexural strength and elastic modulus were measured. The Vickers hardness of fractured specimens was measured on the surface of the cement. Data from viscosity were submitted to oneway ANOVA, while the data from mechanical properties were analyzed by two-way ANOVA. All pair-wise comparisons were performed using Tukey’s test (α = 0.05).

Results: The experimental cement with 68wt% of filler showed the highest viscosity and those with 60wt% showed the the lowest viscosity. Irrespective of the time spent before light-curing, the cement with 65wt% of filler presented the highest values of flexural strength and elastic modulus. The addition of 60wt% of filler resulted in the lowest elastic modulus, while 68wt% of filler resulted in lowest flexural strength. Regarding the hardness, the cement with 68wt% of filler showed the highest values, while there was no difference between 60 and 65wt% of filler.

Conclusion: Filler content affected the mechanical properties of the experimental cement and this effect did not depend on the waiting time before the light-curing procedure.

Keywords: Barium glass filler, dental cements, elastic modulus, flexural strength, hardness, polymerization, resin luting agents.

Graphical Abstract

[1]
Faria e Silva AL, Casselli DS, Ambrosano GM, Martins LR. Effect of the adhesive application mode and fiber post translucency on the push-out bond strength to dentin. J Endod 2007; 33(9): 1078-81.
[http://dx.doi.org/10.1016/j.joen.2007.03.018] [PMID: 17931937]
[2]
Ferrari M, Cagidiaco MC, Goracci C, et al. Long-term retrospective study of the clinical performance of fiber posts. Am J Dent 2007; 20(5): 287-91.
[PMID: 17993023]
[3]
Hikasa T, Matsuka Y, Mine A, et al. A 15-year clinical comparative study of the cumulative survival rate of cast metal core and resin core restorations luted with adhesive resin cement. Int J Prosthodont 2010; 23(5): 397-405.
[PMID: 20859553]
[4]
Faria-e-Silva AL, Menezes Mde S, Silva FP, Reis GR, Moraes RR. Intra-radicular dentin treatments and retention of fiber posts with self-adhesive resin cements. Braz Oral Res 2013; 27(1): 14-9.
[http://dx.doi.org/10.1590/S1806-83242013000100003] [PMID: 23306622]
[5]
Peumans M, Voet M, De Munck J, Van Landuyt K, Van Ende A, Van Meerbeek B. Four-year clinical evaluation of a self-adhesive luting agent for ceramic inlays. Clin Oral Investig 2013; 17(3): 739-50.
[http://dx.doi.org/10.1007/s00784-012-0762-9] [PMID: 22707232]
[6]
Faria-e-Silva AL, Peixoto AC, Borges MG, Menezes Mde S, Moraes RR. Immediate and delayed photoactivation of self-adhesive resin cements and retention of glass-fiber posts. Braz Oral Res 2014; 28: 28.
[http://dx.doi.org/10.1590/S1806-83242014.50000005] [PMID: 25006624]
[7]
Brondani LP, Pereira-Cenci T, Wandsher VF, Pereira GK, Valandro LF, Bergoli CD. Longevity of metal-ceramic crowns cemented with self-adhesive resin cement: a prospective clinical study. Braz Oral Res 2017; 31e22
[http://dx.doi.org/10.1590/1807-3107bor-2017.vol31.0022] [PMID: 28403329]
[8]
Kern M, Passia N, Sasse M, Yazigi C. Ten-year outcome of zirconia ceramic cantilever resin-bonded fixed dental prostheses and the influence of the reasons for missing incisors. J Dent 2017; 65: 51-5.
[http://dx.doi.org/10.1016/j.jdent.2017.07.003] [PMID: 28688950]
[9]
Yamin PA, Pereira RD, Lopes FC, et al. Longevity of bond strength of resin cements to root dentine after radiation therapy. Int Endod J 2018; 51(11): 1301-12.
[http://dx.doi.org/10.1111/iej.12945] [PMID: 29729026]
[10]
Edelhoff D, Ozcan M. To what extent does the longevity of fixed dental prostheses depend on the function of the cement? Working Group 4 materials: cementation. Clin Oral Implants Res 2007; 18(Suppl. 3): 193-204.
[http://dx.doi.org/10.1111/j.1600-0501.2007.01442.x] [PMID: 17594382]
[11]
Irie M, Maruo Y, Nishigawa G, Suzuki K, Watts DC. Physical properties of dual-cured luting-agents correlated to early no interfacial-gap incidence with composite inlay restorations. Dent Mater 2010; 26(6): 608-15.
[http://dx.doi.org/10.1016/j.dental.2010.02.012] [PMID: 20334906]
[12]
Sjögren G, Molin M, van Dijken JW. A 10-year prospective evaluation of CAD/CAM-manufactured (Cerec) ceramic inlays cemented with a chemically cured or dual-cured resin composite. Int J Prosthodont 2004; 17(2): 241-6.
[PMID: 15119879]
[13]
Faria e Silva AL, Arias VG, Soares LES, Martin AA, Martins LRM. Influence of fiber-post translucency on the degree of conversion of a dual-cured resin cement. J Endod 2007; 33(3): 303-5.
[http://dx.doi.org/10.1016/j.joen.2006.11.015] [PMID: 17320720]
[14]
Ho Y-C, Lai Y-L, Chou I-C, Yang S-F, Lee S-Y. Effects of light attenuation by fibre posts on polymerization of a dual-cured resin cement and microleakage of post-restored teeth. J Dent 2011; 39(4): 309-15.
[http://dx.doi.org/10.1016/j.jdent.2011.01.009] [PMID: 21291948]
[15]
Dogar A, Altintas SC, Kavlak S, Guner A. Determining the influence of fibre post light transmission on polymerization depth and viscoelastic behaviour of dual-cured resin cement. Int Endod J 2012; 45(12): 1135-40.
[http://dx.doi.org/10.1111/j.1365-2591.2012.02085.x] [PMID: 22803825]
[16]
Faria-e-Silva AL, Mendonça AA, Garcez RM, Oliveira Ada S, Moreira AG, Moraes RR. Adhesion strategy and early bond strengths of glass-fiber posts luted into root canals. Braz Oral Res 2012; 26(5): 485-7.
[http://dx.doi.org/10.1590/S1806-83242012005000017] [PMID: 22892880]
[17]
Ilie N, Stawarczyk B. Quantification of the amount of light passing through zirconia: the effect of material shade, thickness, and curing conditions. J Dent 2014; 42(6): 684-90.
[http://dx.doi.org/10.1016/j.jdent.2014.03.007] [PMID: 24657553]
[18]
Lu H, Mehmood A, Chow A, Powers JM. Influence of polymerization mode on flexural properties of esthetic resin luting agents. J Prosthet Dent 2005; 94(6): 549-54.
[http://dx.doi.org/10.1016/j.prosdent.2005.09.016] [PMID: 16316801]
[19]
Yoshida K, Tsuo Y, Meng X, Atsuta M. Mechanical properties of dual-cured resin luting agents for ceramic restoration. J Prosthodont 2007; 16(5): 370-6.
[http://dx.doi.org/10.1111/j.1532-849X.2007.00221.x] [PMID: 17672836]
[20]
Tango RN, Sinhoreti MA, Correr AB, Correr-Sobrinho L, Henriques GE. Effect of light-curing method and cement activation mode on resin cement knoop hardness. J Prosthodont 2007; 16(6): 480-4.
[http://dx.doi.org/10.1111/j.1532-849X.2007.00234.x] [PMID: 17760867]
[21]
Pereira SG, Fulgêncio R, Nunes TG, Toledano M, Osorio R, Carvalho RM. Effect of curing protocol on the polymerization of dual-cured resin cements. Dent Mater 2010; 26(7): 710-8.
[http://dx.doi.org/10.1016/j.dental.2010.03.016] [PMID: 20381853]
[22]
Arrais CA, Kasaz Ade C, Albino LG, Rodrigues JA, Reis AF. Effect of curing mode on the hardness of dual-cured composite resin core build-up materials. Braz Oral Res 2010; 24(2): 245-9.
[http://dx.doi.org/10.1590/S1806-83242010000200019] [PMID: 20658046]
[23]
Faria-e-Silva AL, Fabião MM, Arias VG, Martins LR. Activation mode effects on the shear bond strength of dual-cured resin cements. Oper Dent 2010; 35(5): 515-21.
[http://dx.doi.org/10.2341/10-051-L] [PMID: 20945742]
[24]
Ilie N, Simon A. Effect of curing mode on the micro-mechanical properties of dual-cured self-adhesive resin cements. Clin Oral Investig 2012; 16(2): 505-12.
[http://dx.doi.org/10.1007/s00784-011-0527-x] [PMID: 21350865]
[25]
Faria-e-Silva AL, Piva E, Lima GS, Boaro LC, Braga RR, Martins LR. Effect of immediate and delayed light activation on the mechanical properties and degree of conversion in dual-cured resin cements. J Oral Sci 2012; 54(3): 261-6.
[http://dx.doi.org/10.2334/josnusd.54.261] [PMID: 23047037]
[26]
Braga RR, Ballester RY, Ferracane JL. Factors involved in the development of polymerization shrinkage stress in resin-composites: a systematic review. Dent Mater 2005; 21(10): 962-70.
[http://dx.doi.org/10.1016/j.dental.2005.04.018] [PMID: 16085301]
[27]
Al Sunbul H, Silikas N, Watts DC. Polymerization shrinkage kinetics and shrinkage-stress in dental resin-composites. Dent Mater 2016; 32(8): 998-1006.
[http://dx.doi.org/10.1016/j.dental.2016.05.006] [PMID: 27240744]
[28]
Soares CJ, Faria-E-Silva AL, Rodrigues MP, et al. Polymerization shrinkage stress of composite resins and resin cements - What do we need to know? Braz Oral Res 2017; 31(Suppl. 1).e62
[http://dx.doi.org/10.1590/1807-3107bor-2017.vol31.0062] [PMID: 28902242]
[29]
Macedo VC, Faria e Silva AL, Martins LR. Effect of cement type, relining procedure, and length of cementation on pull-out bond strength of fiber posts. J Endod 2010; 36(9): 1543-6.
[http://dx.doi.org/10.1016/j.joen.2010.04.014] [PMID: 20728724]
[30]
Jongsma LA, Ir Nde J, Kleverlaan CJ, Feilzer AJ. Reduced contraction stress formation obtained by a two-step cementation procedure for fiber posts. Dent Mater 2011; 27(7): 670-6.
[http://dx.doi.org/10.1016/j.dental.2011.03.008] [PMID: 21514652]
[31]
Ferracane JL, Hilton TJ. Polymerization stress--is it clinically meaningful? Dent Mater 2016; 32(1): 1-10.
[http://dx.doi.org/10.1016/j.dental.2015.06.020] [PMID: 26220776]
[32]
Wang Z, Chiang MY. Correlation between polymerization shrinkage stress and C-factor depends upon cavity compliance. Dent Mater 2016; 32(3): 343-52.
[http://dx.doi.org/10.1016/j.dental.2015.11.003] [PMID: 26778403]
[33]
Wang Z, Chiang MY. System compliance dictates the effect of composite filler content on polymerization shrinkage stress. Dent Mater 2016; 32(4): 551-60.
[http://dx.doi.org/10.1016/j.dental.2016.01.006] [PMID: 26916062]
[34]
Shouha PSR, Ellakwa AE. Effect of short glass fibers on the polymerization shrinkage stress of dental composite. J Biomed Mater Res B Appl Biomater 2017; 105(7): 1930-7.
[http://dx.doi.org/10.1002/jbm.b.33723] [PMID: 27292231]
[35]
Yamamoto T, Kubota Y, Momoi Y, Ferracane JL. Polymerization stresses in low-shrinkage dental resin composites measured by crack analysis. Dent Mater 2012; 28(9): e143-9.
[http://dx.doi.org/10.1016/j.dental.2012.04.015] [PMID: 22579102]
[36]
Rosatto CM, Bicalho AA, Verí-ssimo C, et al. Mechanical properties, shrinkage stress, cuspal strain and fracture resistance of molars restored with bulk-fill composites and incremental filling technique. J Dent 2015; 43(12): 1519-28.
[http://dx.doi.org/10.1016/j.jdent.2015.09.007] [PMID: 26449641]
[37]
Vukicevic AM, Zelic K, Jovicic G, Djuric M, Filipovic N. Influence of dental restorations and mastication loadings on dentine fatigue behaviour: Image-based modelling approach. J Dent 2015; 43(5): 556-67.
[http://dx.doi.org/10.1016/j.jdent.2015.02.011] [PMID: 25731157]
[38]
Pereira R, Bicalho AA, Franco SD, Tantbirojn D, Versluis A, Soares CJ. Effect of Restorative protocol on cuspal strain and residual stress in endodontically treated molars. Oper Dent 2016; 41(1): 23-33.
[http://dx.doi.org/10.2341/14-178-L] [PMID: 26237644]
[39]
Oliveira LRS, Braga SSL, Bicalho AA, Ribeiro MTH, Price RB, Soares CJ. Molar cusp deformation evaluated by micro-CT and enamel crack formation to compare incremental and bulk-filling techniques. J Dent 2018; 74: 71-8.
[http://dx.doi.org/10.1016/j.jdent.2018.04.015] [PMID: 29689293]
[40]
Tay FR, Loushine RJ, Lambrechts P, Weller RN, Pashley DH. Geometric factors affecting dentin bonding in root canals: a theoretical modeling approach. J Endod 2005; 31(8): 584-9.
[http://dx.doi.org/10.1097/01.don.0000168891.23486.de] [PMID: 16044041]
[41]
Ellakwa A, Cho N, Lee IB. The effect of resin matrix composition on the polymerization shrinkage and rheological properties of experimental dental composites. Dent Mater 2007; 23(10): 1229-35.
[http://dx.doi.org/10.1016/j.dental.2006.11.004] [PMID: 17182093]
[42]
Watts DC, Satterthwaite JD. Axial shrinkage-stress depends upon both C-factor and composite mass. Dent Mater 2008; 24(1): 1-8.
[http://dx.doi.org/10.1016/j.dental.2007.08.007] [PMID: 17920115]
[43]
Gonçalves F, Azevedo CL, Ferracane JL, Braga RR. BisGMA/TEGDMA ratio and filler content effects on shrinkage stress. Dent Mater 2011; 27(6): 520-6.
[http://dx.doi.org/10.1016/j.dental.2011.01.007] [PMID: 21371746]
[44]
Boaro LC, Brandt WC, Meira JB, Rodrigues FP, Palin WM, Braga RR. Experimental and FE displacement and polymerization stress of bonded restorations as a function of the C-Factor, volume and substrate stiffness. J Dent 2014; 42(2): 140-8.
[http://dx.doi.org/10.1016/j.jdent.2013.11.016] [PMID: 24296164]
[45]
Faria-e-Silva A, Boaro L, Braga R, Piva E, Arias V, Martins L. Effect of immediate or delayed light activation on curing kinetics and shrinkage stress of dual-cure resin cements. Oper Dent 2011; 36(2): 196-204.
[http://dx.doi.org/10.2341/10-153-L] [PMID: 21777101]
[46]
Pereira RD, Vald-via AD, Bicalho AA, et al. Effect of Photoactivation Timing on the Mechanical Properties of Resin Cements and Bond Strength of Fiberglass Post to Root Dentin. Oper Dent 2015; 40(5): E206-21.
[http://dx.doi.org/10.2341/14-115-L] [PMID: 26237639]
[47]
Faria-E-Silva AL, Pfeifer CS. Delayed photo-activation and addition of thio-urethane: Impact on polymerization kinetics and stress of dual-cured resin cements. J Dent 2017; 65: 101-9.
[http://dx.doi.org/10.1016/j.jdent.2017.07.014] [PMID: 28750778]
[48]
Khoroushi M, Ghasemi M, Abedinzadeh R, Samimi P. Comparison of immediate and delayed light-curing on nano-indentation creep and contraction stress of dual-cured resin cements. J Mech Behav Biomed Mater 2016; 64: 272-80.
[http://dx.doi.org/10.1016/j.jmbbm.2016.08.001] [PMID: 27544311]
[49]
Soares CJ, Bicalho AA, Verissimo C, Soares P, Tantbirojn D, Versluis A. Delayed Photo-activation Effects on Mechanical Properties of Dual Cured Resin Cements and Finite Element Analysis of Shrinkage Stresses in Teeth Restored With Ceramic Inlays. Oper Dent 2016; 41(5): 491-500.
[http://dx.doi.org/10.2341/15-090-L] [PMID: 26794188]
[50]
Feng L, Suh BI. A mechanism on why slower polymerization of a dental composite produces lower contraction stress. J Biomed Mater Res B Appl Biomater 2006; 78(1): 63-9.
[http://dx.doi.org/10.1002/jbm.b.30453] [PMID: 16470813]
[51]
F e Silva AL. Pereira GD, Dias CT, Sartini Paulillo LA. Effect of the composite photoactivation mode on microtensile bond strength and Knoop microhardness. Dent Mater 2006; 22(3): 203-10.
[http://dx.doi.org/10.1016/j.dental.2005.04.017] [PMID: 16098575]
[52]
Feng L, Suh BI. The effect of curing modes on polymerization contraction stress of a dual cured composite. J Biomed Mater Res B Appl Biomater 2006; 76(1): 196-202.
[http://dx.doi.org/10.1002/jbm.b.30355] [PMID: 16047326]
[53]
Charton C, Colon P, Pla F. Shrinkage stress in light-cured composite resins: influence of material and photoactivation mode. Dent Mater 2007; 23(8): 911-20.
[http://dx.doi.org/10.1016/j.dental.2006.06.034] [PMID: 17027939]
[54]
Ilie N, Jelen E, Hickel R. Is the soft-start polymerisation concept still relevant for modern curing units? Clin Oral Investig 2011; 15(1): 21-9.
[http://dx.doi.org/10.1007/s00784-009-0354-5] [PMID: 19937074]
[55]
Lu H, Stansbury JW, Bowman CN. Impact of curing protocol on conversion and shrinkage stress. J Dent Res 2005; 84(9): 822-6.
[http://dx.doi.org/10.1177/154405910508400908] [PMID: 16109991]
[56]
Tauböck TT, Jäger F, Attin T. Polymerization shrinkage and shrinkage force kinetics of high- and low-viscosity dimethacrylate- and ormocer-based bulk-fill resin composites. Odontology 2019; 107(1): 103-10.
[http://dx.doi.org/10.1007/s10266-018-0369-y] [PMID: 29948491]
[57]
El-Damanhoury H, Platt J. Polymerization shrinkage stress kinetics and related properties of bulk-fill resin composites. Oper Dent 2014; 39(4): 374-82.
[http://dx.doi.org/10.2341/13-017-L] [PMID: 23865582]
[58]
Son SA, Park JK, Seo DG, Ko CC, Kwon YH. How light attenuation and filler content affect the microhardness and polymerization shrinkage and translucency of bulk-fill composites? Clin Oral Investig 2017; 21(2): 559-65.
[http://dx.doi.org/10.1007/s00784-016-1920-2] [PMID: 27475636]
[59]
ISO 4049:2009. Dentistry-resin based filling materials. International Organization for Standardization 2009..
[http://dx.doi.org/10.14393/BJ-v32n3a2016-31056]
[60]
Oliveira AC, Barreto CM, Oliveira-Neto LA, Moraes RR, Faria-e-Silva AL. An alternative specimen preparation technique for 3-point bending tests on dual-cured dental resin cements. Biosci J 2016; 32: 822-8.
[http://dx.doi.org/10.14393/BJ-v32n3a2016-31056]
[61]
Lovell LG, Newman SM, Bowman CN. The effects of light intensity, temperature, and comonomer composition on the polymerization behavior of dimethacrylate dental resins. J Dent Res 1999; 78(8): 1469-76.
[http://dx.doi.org/10.1177/00220345990780081301] [PMID: 10439035]
[62]
Charton C, Falk V, Marchal P, Pla F, Colon P. Influence of Tg, viscosity and chemical structure of monomers on shrinkage stress in light-cured dimethacrylate-based dental resins. Dent Mater 2007; 23(11): 1447-59.
[http://dx.doi.org/10.1016/j.dental.2007.05.017] [PMID: 17719627]
[63]
Steinhaus J, Hausnerova B, Haenel T, Selig D, Duvenbeck F, Moeginger B. Correlation of shear and dielectric ion viscosity of dental resins - Influence of composition, temperature and filler content. Dent Mater 2016; 32(7): 899-907.
[http://dx.doi.org/10.1016/j.dental.2016.03.015] [PMID: 27130611]
[64]
Amirouche-Korichi A, Mouzali M, Watts DC. Effects of monomer ratios and highly radiopaque fillers on degree of conversion and shrinkage-strain of dental resin composites. Dent Mater 2009; 25(11): 1411-8.
[http://dx.doi.org/10.1016/j.dental.2009.06.009] [PMID: 19683808]
[65]
Gonçalves F, Kawano Y, Pfeifer C, Stansbury JW, Braga RR. Influence of BisGMA, TEGDMA, and BisEMA contents on viscosity, conversion, and flexural strength of experimental resins and composites. Eur J Oral Sci 2009; 117(4): 442-6.
[http://dx.doi.org/10.1111/j.1600-0722.2009.00636.x] [PMID: 19627357]
[66]
Moraes RR, Garcia JW, Barros MD, et al. Control of polymerization shrinkage and stress in nanogel-modified monomer and composite materials. Dent Mater 2011; 27(6): 509-19.
[http://dx.doi.org/10.1016/j.dental.2011.01.006] [PMID: 21388669]
[67]
Tauböck TT, Tarle Z, Marovic D, Attin T. Pre-heating of high-viscosity bulk-fill resin composites: effects on shrinkage force and monomer conversion. J Dent 2015; 43(11): 1358-64.
[http://dx.doi.org/10.1016/j.jdent.2015.07.014] [PMID: 26232610]
[68]
Kim KH, Ong JL, Okuno O. The effect of filler loading and morphology on the mechanical properties of contemporary composites. J Prosthet Dent 2002; 87(6): 642-9.
[http://dx.doi.org/10.1067/mpr.2002.125179] [PMID: 12131887]
[69]
Labella R, Lambrechts P, Van Meerbeek B, Vanherle G. Polymerization shrinkage and elasticity of flowable composites and filled adhesives. Dent Mater 1999; 15(2): 128-37.
[http://dx.doi.org/10.1016/S0109-5641(99)00022-6] [PMID: 10551104]
[70]
Sakaguchi RL, Wiltbank BD, Murchison CF. Prediction of composite elastic modulus and polymerization shrinkage by computational micromechanics. Dent Mater 2004; 20(4): 397-401.
[http://dx.doi.org/10.1016/j.dental.2003.11.003] [PMID: 15019456]
[71]
Min SH, Ferracane J, Lee IB. Effect of shrinkage strain, modulus, and instrument compliance on polymerization shrinkage stress of light-cured composites during the initial curing stage. Dent Mater 2010; 26(10): 1024-33.
[http://dx.doi.org/10.1016/j.dental.2010.07.002] [PMID: 20684977]
[72]
Song HB, Sowan N, Shah PK, et al. Reduced shrinkage stress via photo-initiated copper(I)-catalyzed cycloaddition polymerizations of azide-alkyne resins. Dent Mater 2016; 32(11): 1332-42.
[http://dx.doi.org/10.1016/j.dental.2016.07.014] [PMID: 27524230]
[73]
Aregawi WA, Fok ASL. 1/(2+Rc): A simple predictive formula for laboratory shrinkage-stress measurement. Dent Mater 2017; 33(5): 536-42.
[http://dx.doi.org/10.1016/j.dental.2017.03.012] [PMID: 28377042]
[74]
Pereira SG, Telo JP, Nunes TG. Towards a controlled photopolymerization of dental dimethacrylate monomers: EPR studies on effects of dilution, filler loading, storage and aging. J Mater Sci Mater Med 2008; 19(9): 3135-44.
[http://dx.doi.org/10.1007/s10856-008-3434-1] [PMID: 18415003]
[75]
Yap AU, Soh MS, Han TT, Siow KS. Influence of curing lights and modes on cross-link density of dental composites. Oper Dent 2004; 29(4): 410-5.
[PMID: 15279480]
[76]
Feitosa VP, Fugolin AP, Correr AB, et al. Effects of different photo-polymerization protocols on resin-dentine μTBS, mechanical properties and cross-link density of a nano-filled resin composite. J Dent 2012; 40(10): 802-9.
[http://dx.doi.org/10.1016/j.jdent.2012.05.014] [PMID: 22687576]
[77]
Rastelli AN, Jacomassi DP, Faloni AP, et al. The filler content of the dental composite resins and their influence on different properties. Microsc Res Tech 2012; 75(6): 758-65.
[http://dx.doi.org/10.1002/jemt.21122] [PMID: 22213178]

Rights & Permissions Print Cite
Article Metrics
11
© 2024 Bentham Science Publishers | Privacy Policy