Abstract
In this paper, we report the synthesis of barium zirconate, BaZrO3, (BZ) nanotubes fabricated by the modified sol-gel method within the nanochannels of anodic aluminum oxide (AAO) templates. The morphology, structure, and composition of as prepared nanotubes were characterized by means of X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM), selected-area electron diffraction (SAED), high resolution TEM (HRTEM) and energy-dispersive X-ray spectroscopy (EDX). The results of XRD and SAED indicated that postannealed (at 650°C for 1 h) BZ nanotubes (BZNTs) exhibited a polycrystalline cubic perovskite crystal structure. SEM and TEM analysis revealed that BZNTs possessed a uniform length and diameter (∼200 nm) and the thickness of the wall of the BZNTs was about 20 nm. Y-junctions, multiple branching and typical T-junctions were also observed in some BZNTs. EDX analysis demonstrated that stoichiometric BaZrO3 was formed. HRTEM image confirmed that the obtained BZNTs were composed of nanoparticles in the range of 5-10 nm. The possible formation mechanism of BZNTs was discussed.
Keywords: Nanofabrication, nanotubes, Y-junctions, electron microscopy, barium zirconato
Related Books
The Art of Nanomaterials
Advanced Materials and Nano Systems: Theory and Experiment - Part 2
Advanced Materials and Nano Systems: Theory and Experiment (Part-1)
Artificial Intelligence for Smart Cities and Villages: Advanced Technologies, Development, and Challenges
SILVER NANOPARTICLES: Synthesis, Functionalization and Applications
2